WBM7079 is a synthetic paper-based short-term removable sticker. It provides excellent adhesion on many surfaces including PET, glass, and metal, and can be removed easily without leaving any residue.
weight | thickness | material | |
Face Material | 70 g / m² ± 10% ISO536 | 0.09mm ± 10% ISO534 | Uncoated white matte paper |
Liner | 80 g / m² ± 10% ISO536 | 0.8mm ± 10% ISO534 | Monochrome coated white CCK release paper |
Adhesive | ER is an acrylic adhesive with weak viscosity and is not suitable for repeated pasting. It is not suitable for pasting PE or PVC products, and it is not recommended to apply it to the surface with oil. | ||
Peel adhesion | initial adhesion 5 N/25mm or tear off FTM9 | 20 mins Peel adhesion value on steel at 180 angle 3.5 N/25mm or tear off FTM1 | 20 mins Peel adhesion value on steel at 90 angle 3N/25mm or tear off FTM2 |
Temperature | Min. Appl. Temp. 10 ºC | Service Temp. 0 ºC +90ºC (24H after labeling) |
This product has good adhesion performance and is widely used in price tags, book labels, computer printed labels and matt labels.
The above suggestion, application, and elaboration are not intended as the guarantee of Jinya. All sales of Jinya products shall be tested by customer in the final environment to confirm compliance with the requirements of the use of environment.
The surface material has excellent ink absorption and is suitable for a variety of printing methods, including laser and inkjet printing. Matte paper with rough surface is suitable for printing and printing simple pictures and texts. It is applied to office, logistics and other industries.
Shelf life
12 months, applicable only to the material delivered by Jinya which has not undergone further processing, under the following STORAGE CONDITIONS:
This material must be stored at a temperature of 23±2ºC and 50±5% of Relative Humidity.
Storage area must be dry and clean.
Keep the material in the original packaging when not used in order to protect it from dust and contamination.
Do not expose to direct sunlight or heat sources.